Fasteners, Connectors and Flashing for Pressure Treated Wood Treated wood is typically used in applications where it may be exposed to moisture for considerable periods so the fasteners and connectors must also be resistant to these conditions. In addition, most wood preservatives designed for exterior use contain copper that may react with the metals used to fabricate fasteners and connectors therefore, it is important to use the right type of fastener and/or connectors. Where treated wood is used in dry environments to prevent damage by wood-destroying insects, including termites, corrosion is of less concern. Users and specifiers should also be aware that corrosive industrial, or salt air, environments may also require the use of appropriate corrosion resistant metals.

Types of Wood Preserving Treatments

Chromated copper arsenate, type C (CCA-C) was until recently the industry’s standard wood preservative, but alternative treatments such as alkaline copper quat (ACQ) and copper azole (CA) have replaced CCA-C in products destined for most exterior residential applications. In addition to these two newer preservatives, sodium borate (SBX) treated lumber is now used for many interior applications. CCA can still be used to treat wood for most industrial, commercial and agricultural uses.

Past Practice

Hot dipped galvanized steel, types 304 or 316 stainless steel fasteners (nails and screws) and copper have always been recommended by the industry for use with treated wood. The thickness of the zinc on hot dip galvanized fasteners and connectors used with CCA treated wood, had never been specified. Zinc coatings conforming to ASTM A653 G60 and G90 grade were commonly used for connectors such as joist hangers and truss plates. Electroplate galvanized steel and aluminum had never been recommended for use in contact with treated wood. When the use of aluminum cannot be avoided, corrosion can be minimized by using spacers or physical barriers to prevent direct contact of the metal with the pressure treated wood.

Current recommendations for galvanized steel connectors and fasteners are similar to past practice, except that by reference to ASTM standards, the minimum requirements for the amount of zinc are higher than those previously used. Note that galvanizing is a sacrificial coating and the presence of some white corrosion product on the surface is normal. Red rust is an indicator of coating failure.

Current Recommendations on Connectors for Treated Wood

Connectors used for ACQ or CA treated wood should be manufactured from steel either galvanized in accordance with ASTM A653, G185 designation, or be galvanized after manufacture in accordance with ASTM A123. Stainless steel connectors (type 304 or 316) are recommended for maximum service life or severe applications. For borate treated wood used inside buildings, the same connectors can be used as for untreated wood.

Current Recommendations on Fasteners for Treated Wood Fasteners for ACQ or CA treated wood should be galvanized in accordance with ASTM A153. Stainless steel can still be used for maximum service life or severe applications. Where appropriate, copper fasteners may also be used. Fasteners used in combination with metal connectors must be the same type of metal to avoid galvanic corrosion caused by dissimilar metals. For example stainless steel fasteners should not be used in combination with galvanized connectors. For borate treated wood used inside buildings, the same fasteners can be used as for untreated wood.

Current Recommendations on Flashing for Treated Wood

Flashing used in contact with treated wood must be compatible with the treated wood and last long enough to be suitable for the intended application. Flashing must also be of the type of metal as any fasteners that penetrate through them to avoid galvanic corrosion. Copper and stainless steel are the most durable metals for flashing. Galvanized steel, in accordance with ASTM A653, G185 designation, is also suitable for use as flashing.

Other fasteners, connectors or hardware as recommended by the manufacturer

There may be additional products such as polymer or ceramic coatings, or vinyl or plastic flashings that are suitable for use with treated wood products. Consult the individual fastener, connector or flashing manufacturer for recommendations for use of their products with treated wood.

For further information on the new preservative products, please visit:

For information on fasteners, visit:

30 March 2005